Comparison

ABS vs PA66

A side-by-side comparison of Acrylonitrile Butadiene Styrene and Polyamide 6,6 (Nylon).

Property

ABS

PA66

Physical

Density

1.04 – 1.07 g/cm³

1.14 g/cm³

Specific Gravity

1.05

—

Water Absorption (24h)

0.20 – 0.45 %

1.2 %

Transparency

Opaque

Surface Finish

Matte to glossy

—

Shrinkage

0.4 – 0.9 %

1.5 – 2.0 %

Mechanical

Young's Modulus

1.8 – 2.5 GPa

3.0 GPa (dry)

Tensile Strength

40 – 50 MPa

80 MPa

Flexural Strength

60 – 80 MPa

110 MPa

Impact Strength (Izod)

200 – 400 J/m

50 J/m

Hardness (Rockwell R)

100 – 115

—

Elongation at Break

10 – 50 %

60 %

Thermal

Glass Transition Temperature

105 °C

70 °C

Melting Point

Amorphous (no true Tm)

255 – 265 °C

Continuous Service Temperature

70 – 90 °C

100 – 120 °C

Heat Deflection Temperature

85 – 100 °C

75 °C (unfilled)

Thermal Conductivity

0.17 W/m·K

—

CTE

80 – 100 × 10⁻⁶ /K

—

Electrical

Dielectric Constant

2.7 – 3.2

4.0

Surface Resistivity

10¹⁵ Ω

—

Volume Resistivity

10¹⁶ Ω·cm

10¹² Ω·cm

Dielectric Strength

15 – 20 kV/mm

—

Chemical resistance

Acids (dilute)

Good

—

Bases

Good

Alcohols

Good

Oils & Greases

Fair

—

Gasoline

Poor

—

Acetone

Attacks / dissolves

—

UV Resistance

Poor (unless stabilized)

Fair

Weathering

Poor without stabilizers

—

Acids

—

Poor

Oils & Fuels

—

Excellent

Sustainability

Recyclability

Recyclable (mechanical)

Recyclable

Recycling Code

7 (Other)

Bio-based Content

0 %

0 – 100 % (bio grades)

Carbon Footprint

~3.1 kg CO₂e / kg

~7.4 kg CO₂e / kg