Comparison
Aromatic Nylon GF vs PA66
A side-by-side comparison of Aromatic Polyamide/Nylon, Glass Fiber Reinforced and Polyamide 6,6 (Nylon).
Physical
Density
1.20-1.35 g/cm³
1.14 g/cm³
Water Absorption (24h)
0.5-1.5 %
1.2 %
Transparency
Opaque
Opaque
Shrinkage
0.3-0.7 %
1.5 – 2.0 %
Mechanical
Young's Modulus
8-15 GPa
3.0 GPa (dry)
Tensile Strength
100-180 MPa
80 MPa
Elongation at Break
3-10 %
60 %
Impact Strength (Izod)
10-30 kJ/m
50 J/m
Flexural Strength
—
110 MPa
Thermal
Glass Transition Temperature
100-150 °C
70 °C
Melting Point
240-290 °C (depending on type)
255 – 265 °C
Continuous Service Temperature
120-160 °C
100 – 120 °C
Heat Deflection Temperature
200-270 °C (1.8 MPa)
75 °C (unfilled)
Electrical
Dielectric Constant
4.0-5.0
4.0
Volume Resistivity
10^9-10^11 Ohm-cm
10¹² Ω·cm
Dielectric Strength
10-15 kV/mm
—
Chemical resistance
Acids
Good
Poor
Bases
Good
Good
Solvents
Good
—
UV Resistance
Fair to Good
Fair
Alcohols
—
Good
Oils & Fuels
—
Excellent
Sustainability
Recyclability
Recyclable
Recyclable
Recycling Code
7 (Other)
7
Carbon Footprint
High
~7.4 kg CO₂e / kg
Bio-based Content
—
0 – 100 % (bio grades)