Comparison
Bio-PA610 Rigid vs PETG
A side-by-side comparison of Bio-based Polyamide 610, Rigid Grade EE and Polyethylene Terephthalate Glycol.
Physical
Density
1.06 g/cm³
1.27 g/cm³
Water Absorption (24h)
1.0 %
0.13 %
Transparency
Opaque
Transparent
Shrinkage
0.8 - 1.5 %
0.2 – 0.5 %
Mechanical
Young's Modulus
2.2 GPa
2.1 GPa
Tensile Strength
60 MPa
50 MPa
Elongation at Break
15 %
120 %
Impact Strength (Izod)
3.0 J/cm
100 J/m
Flexural Strength
—
70 MPa
Thermal
Glass Transition Temperature
45-55 °C
80 °C
Melting Point
220-230 °C
—
Continuous Service Temperature
100-110 °C
65 °C
Heat Deflection Temperature
60-70 °C
70 °C
CTE
—
68 × 10⁻⁶ /K
Electrical
Dielectric Constant
3.9
3.3
Volume Resistivity
10¹¹ Ω·cm
10¹⁴ Ω·cm
Dielectric Strength
26 kV/mm
—
Chemical resistance
Acids
Moderate resistance
Good
Bases
Good resistance
Fair
Solvents
Good resistance to oils, greases; attacked by strong acids
—
UV Resistance
Moderate (requires additive)
Fair
Alcohols
—
Good
Oils
—
Good
Sustainability
Recyclability
Recyclable
Recyclable
Recycling Code
7 (Other)
1
Carbon Footprint
Lower than conventional PA610
~2.7 kg CO₂e / kg
Bio-based Content
—
0 %