Comparison
CAB Injection Molding Grade L vs PA66
A side-by-side comparison of Cellulose Acetate Butyrate, Injection Molding Grade L and Polyamide 6,6 (Nylon).
Physical
Density
1.20 g/cm³
1.14 g/cm³
Water Absorption (24h)
1.0 %
1.2 %
Transparency
Good
Opaque
Shrinkage
0.8 - 1.8 %
1.5 – 2.0 %
Mechanical
Young's Modulus
1.8 GPa
3.0 GPa (dry)
Tensile Strength
35 MPa
80 MPa
Elongation at Break
20.0 %
60 %
Impact Strength (Izod)
1.0 J/cm
50 J/m
Flexural Strength
—
110 MPa
Thermal
Glass Transition Temperature
80-100 °C
70 °C
Melting Point
None (degrades)
255 – 265 °C
Continuous Service Temperature
50 °C
100 – 120 °C
Heat Deflection Temperature
50 °C
75 °C (unfilled)
Electrical
Dielectric Constant
3.3
4.0
Volume Resistivity
10¹¹ Ω·cm
10¹² Ω·cm
Dielectric Strength
16 kV/mm
—
Chemical resistance
Acids
Poor resistance
Poor
Bases
Poor resistance
Good
Solvents
Soluble in esters, ketones, and chlorinated hydrocarbons
—
UV Resistance
Good
Fair
Alcohols
—
Good
Oils & Fuels
—
Excellent
Sustainability
Recyclability
Recyclable (often downcycled)
Recyclable
Recycling Code
7 (Other)
7
Carbon Footprint
Moderate
~7.4 kg CO₂e / kg
Bio-based Content
—
0 – 100 % (bio grades)