Comparison
Chitosan Crosslinked vs Polycarbonate
A side-by-side comparison of Chitosan, Crosslinked Grade DD and Polycarbonate.
Physical
Density
1.45 g/cm³
1.20 g/cm³
Water Absorption (24h)
3.0-6.0 %
0.15 %
Transparency
Good
Transparent (88% light transmission)
Shrinkage
2.5-5.0 %
0.5 – 0.8 %
Mechanical
Young's Modulus
1.5 GPa
2.3 – 2.4 GPa
Tensile Strength
40 MPa
60 – 70 MPa
Elongation at Break
4.0 %
100 – 150 %
Impact Strength (Izod)
0.3 J/cm
600 – 900 J/m
Flexural Strength
—
90 – 100 MPa
Hardness (Rockwell M)
—
70
Thermal
Glass Transition Temperature
90-130 °C
147 °C
Melting Point
None (degrades)
—
Continuous Service Temperature
70 °C
115 – 130 °C
Heat Deflection Temperature
60 °C
130 – 140 °C
Thermal Conductivity
—
0.20 W/m·K
CTE
—
65 – 70 × 10⁻⁶ /K
Electrical
Dielectric Constant
4.8
2.9 – 3.0
Volume Resistivity
10¹¹ Ω·cm
10¹⁶ Ω·cm
Dielectric Strength
16 kV/mm
15 kV/mm
Chemical resistance
Acids
Soluble in dilute acids
—
Bases
Good resistance
Poor
Solvents
Reduced solubility in acidic solutions due to crosslinking
—
UV Resistance
Poor
Poor (unless coated)
Acids (dilute)
—
Good
Alcohols
—
Fair
Oils
—
Good
Gasoline
—
Fair
Acetone
—
Poor (attacks)
Sustainability
Recyclability
Biodegradable (compost)
Recyclable
Recycling Code
7 (Other)
7
Carbon Footprint
Low (utilizes waste streams)
~5 kg CO₂e / kg
Bio-based Content
—
0 – 50 % (bio grades)