Comparison
PC FDM Filament vs PETG
A side-by-side comparison of Polycarbonate Filament for FDM and Polyethylene Terephthalate Glycol.
Physical
Density
1.20-1.22 g/cm³
1.27 g/cm³
Water Absorption (24h)
0.2-0.4 %
0.13 %
Transparency
Transparent to Translucent
Transparent
Shrinkage
Moderate (0.4-0.7%)
0.2 – 0.5 %
Mechanical
Young's Modulus
2.0-2.5 GPa
2.1 GPa
Tensile Strength
60-70 MPa
50 MPa
Elongation at Break
5-10 %
120 %
Impact Strength (Izod)
15-25 kJ/m²
100 J/m
Flexural Strength
—
70 MPa
Thermal
Glass Transition Temperature
130-145 °C
80 °C
Melting Point
230-300 °C (softens)
—
Continuous Service Temperature
100-120 °C
65 °C
Heat Deflection Temperature
120-135 °C @ 1.82 MPa
70 °C
CTE
—
68 × 10⁻⁶ /K
Electrical
Dielectric Constant
3.0-3.2
3.3
Volume Resistivity
10¹³-10¹⁵ Ω·cm
10¹⁴ Ω·cm
Dielectric Strength
15-20 MV/m
—
Chemical resistance
Acids
Resistant to dilute acids
Good
Bases
Attacked by strong bases
Fair
Solvents
Attacked by ketones, esters, chlorinated hydrocarbons. Attacked by NaOH.
—
UV Resistance
Moderate (can yellow)
Fair
Alcohols
—
Good
Oils
—
Good
Sustainability
Recyclability
Recyclable (within PC stream)
Recyclable
Recycling Code
7 (Other)
1
Carbon Footprint
High
~2.7 kg CO₂e / kg
Bio-based Content
—
0 %