Comparison
High-Temp SLA Resin vs PLA
A side-by-side comparison of High-Temperature Photopolymer Resin for SLA and Polylactic Acid.
Physical
Density
1.15-1.25 g/cm³
1.24 g/cm³
Water Absorption (24h)
0.2-0.4 %
0.5 %
Transparency
Opaque
Semi-transparent
Shrinkage
Moderate (1-3%)
0.3 – 0.5 %
Mechanical
Young's Modulus
2.5-3.5 GPa
3.5 GPa
Tensile Strength
45-60 MPa
50 – 65 MPa
Elongation at Break
3-6 %
6 %
Impact Strength (Izod)
2-4 kJ/m²
16 J/m
Flexural Strength
—
80 MPa
Thermal
Glass Transition Temperature
150-250 °C
60 °C
Melting Point
N/A (cross-linked polymer)
150 – 160 °C
Continuous Service Temperature
120-180 °C
45 °C
Heat Deflection Temperature
140-200 °C @ 1.82 MPa
55 °C
Electrical
Dielectric Constant
3.0-3.5
3.0
Volume Resistivity
10¹²-10¹⁴ Ω·cm
10¹⁴ Ω·cm
Dielectric Strength
15-20 MV/m
—
Chemical resistance
Acids
Fair resistance
Fair
Bases
Poor resistance
Poor
Solvents
Attacked by strong solvents.
—
UV Resistance
Poor
Poor
Alcohols
—
Fair
Hydrolysis
—
Poor
Sustainability
Recyclability
Not Recyclable
Industrially compostable
Recycling Code
N/A
7
Carbon Footprint
High
~1.6 kg CO₂e / kg
Bio-based Content
—
100 %