Comparison
PBAT High Heat vs PLA
A side-by-side comparison of Poly(butylene adipate-co-terephthalate), High Heat Grade BB and Polylactic Acid.
Physical
Density
1.21 g/cm³
1.24 g/cm³
Water Absorption (24h)
0.45 %
0.5 %
Transparency
Good
Semi-transparent
Shrinkage
1.2 - 2.8 %
0.3 – 0.5 %
Mechanical
Young's Modulus
0.35 GPa
3.5 GPa
Tensile Strength
32 MPa
50 – 65 MPa
Elongation at Break
350-550 %
6 %
Impact Strength (Izod)
2.8 J/cm
16 J/m
Flexural Strength
—
80 MPa
Thermal
Glass Transition Temperature
-45 °C
60 °C
Melting Point
118-128 °C
150 – 160 °C
Continuous Service Temperature
50 °C
45 °C
Heat Deflection Temperature
35 °C
55 °C
Electrical
Dielectric Constant
2.9
3.0
Volume Resistivity
10¹³ Ω·cm
10¹⁴ Ω·cm
Dielectric Strength
17 kV/mm
—
Chemical resistance
Acids
Good resistance
Fair
Bases
Good resistance
Poor
Solvents
Resistant to aliphatic hydrocarbons, but swells in chlorinated solvents
—
UV Resistance
Poor
Poor
Alcohols
—
Fair
Hydrolysis
—
Poor
Sustainability
Recyclability
Biodegradable (compost)
Industrially compostable
Recycling Code
7 (Other)
7
Carbon Footprint
Lower than fossil-based plastics
~1.6 kg CO₂e / kg
Bio-based Content
—
100 %