Comparison
PBSA Copolymer Grade H vs PA66
A side-by-side comparison of Polybutylene Succinate Adipate, Copolymer Grade H and Polyamide 6,6 (Nylon).
Physical
Density
1.24 g/cm³
1.14 g/cm³
Water Absorption (24h)
0.6 %
1.2 %
Transparency
Good
Opaque
Shrinkage
2.0 - 3.5 %
1.5 – 2.0 %
Mechanical
Young's Modulus
0.4 GPa
3.0 GPa (dry)
Tensile Strength
30 MPa
80 MPa
Elongation at Break
20.0 %
60 %
Impact Strength (Izod)
1.5 J/cm
50 J/m
Flexural Strength
—
110 MPa
Thermal
Glass Transition Temperature
-15 °C
70 °C
Melting Point
95-105 °C
255 – 265 °C
Continuous Service Temperature
40 °C
100 – 120 °C
Heat Deflection Temperature
30 °C
75 °C (unfilled)
Electrical
Dielectric Constant
2.9
4.0
Volume Resistivity
10¹³ Ω·cm
10¹² Ω·cm
Dielectric Strength
17 kV/mm
—
Chemical resistance
Acids
Good resistance
Poor
Bases
Good resistance
Good
Solvents
Resistant to aliphatic hydrocarbons, but swells in chlorinated solvents
—
UV Resistance
Moderate
Fair
Alcohols
—
Good
Oils & Fuels
—
Excellent
Sustainability
Recyclability
Biodegradable (compost)
Recyclable
Recycling Code
7 (Other)
7
Carbon Footprint
Lower than petrochemical plastics
~7.4 kg CO₂e / kg
Bio-based Content
—
0 – 100 % (bio grades)