PDLA Stereocomplex Grade C vs PLA
A side-by-side comparison of Poly(D-lactic acid), Stereocomplex Grade C and Polylactic Acid.
Physical
Density
1.27 g/cm³
1.24 g/cm³
Water Absorption (24h)
0.25 %
0.5 %
Transparency
Good
Semi-transparent
Shrinkage
1.5 - 4.0 %
0.3 – 0.5 %
Mechanical
Young's Modulus
4.0 GPa
3.5 GPa
Tensile Strength
65 MPa
50 – 65 MPa
Elongation at Break
2.0 %
6 %
Impact Strength (Izod)
0.2 J/cm
16 J/m
Flexural Strength
—
80 MPa
Thermal
Glass Transition Temperature
55-60 °C
60 °C
Melting Point
220-230 °C (stereocomplex)
150 – 160 °C
Continuous Service Temperature
70 °C
45 °C
Heat Deflection Temperature
75 °C
55 °C
Electrical
Dielectric Constant
3.5
3.0
Volume Resistivity
10¹¹ Ω·cm
10¹⁴ Ω·cm
Dielectric Strength
25 kV/mm
—
Chemical resistance
Acids
Poor resistance
Fair
Bases
Poor resistance
Poor
Solvents
Resistant to oils and greases, but swells in chlorinated hydrocarbons
—
UV Resistance
Poor
Poor
Alcohols
—
Fair
Hydrolysis
—
Poor
Sustainability
Recyclability
Compostable (industrial)
Industrially compostable
Recycling Code
7 (Other)
7
Carbon Footprint
Lower than fossil-based plastics
~1.6 kg CO₂e / kg
Bio-based Content
—
100 %