Comparison
Lightweight Flexible Polyamide Elastomer (Pebax) vs PA66
A side-by-side comparison of Polyamide Elastomer (TPA - Pebax® family) and Polyamide 6,6 (Nylon).
Physical
Density
0.98 - 1.05 g/cm³
1.14 g/cm³
Water Absorption (24h)
0.5 - 1.5 %
1.2 %
Transparency
Opaque to Translucent
Opaque
Shrinkage
0.5 - 1.5 %
1.5 – 2.0 %
Mechanical
Young's Modulus
0.005 - 0.05 GPa
3.0 GPa (dry)
Tensile Strength
20 - 50 MPa
80 MPa
Elongation at Break
400 - 800 %
60 %
Impact Strength (Izod)
Good (especially notched)
50 J/m
Flexural Strength
—
110 MPa
Thermal
Glass Transition Temperature
-50 to -20 °C
70 °C
Melting Point
100 - 180 °C
255 – 265 °C
Continuous Service Temperature
-40 to 90 °C
100 – 120 °C
Heat Deflection Temperature
30 - 60 °C
75 °C (unfilled)
Electrical
Dielectric Constant
3.0 - 4.0
4.0
Volume Resistivity
10^12 - 10^14 Ohm-cm
10¹² Ω·cm
Dielectric Strength
15 - 25 kV/mm
—
Chemical resistance
Acids
Good
Poor
Bases
Good
Good
Solvents
Good resistance to oils, greases; swells in strong polar solvents
—
UV Resistance
Good
Fair
Alcohols
—
Good
Oils & Fuels
—
Excellent
Sustainability
Recyclability
Recyclable (thermoplastic)
Recyclable
Recycling Code
7 (Other)
7
Carbon Footprint
Moderate to High
~7.4 kg CO₂e / kg
Bio-based Content
—
0 – 100 % (bio grades)