Comparison
Lightweight Flexible Polyamide Elastomer (Pebax) vs PLA
A side-by-side comparison of Polyamide Elastomer (TPA - Pebax® family) and Polylactic Acid.
Physical
Density
0.98 - 1.05 g/cm³
1.24 g/cm³
Water Absorption (24h)
0.5 - 1.5 %
0.5 %
Transparency
Opaque to Translucent
Semi-transparent
Shrinkage
0.5 - 1.5 %
0.3 – 0.5 %
Mechanical
Young's Modulus
0.005 - 0.05 GPa
3.5 GPa
Tensile Strength
20 - 50 MPa
50 – 65 MPa
Elongation at Break
400 - 800 %
6 %
Impact Strength (Izod)
Good (especially notched)
16 J/m
Flexural Strength
—
80 MPa
Thermal
Glass Transition Temperature
-50 to -20 °C
60 °C
Melting Point
100 - 180 °C
150 – 160 °C
Continuous Service Temperature
-40 to 90 °C
45 °C
Heat Deflection Temperature
30 - 60 °C
55 °C
Electrical
Dielectric Constant
3.0 - 4.0
3.0
Volume Resistivity
10^12 - 10^14 Ohm-cm
10¹⁴ Ω·cm
Dielectric Strength
15 - 25 kV/mm
—
Chemical resistance
Acids
Good
Fair
Bases
Good
Poor
Solvents
Good resistance to oils, greases; swells in strong polar solvents
—
UV Resistance
Good
Poor
Alcohols
—
Fair
Hydrolysis
—
Poor
Sustainability
Recyclability
Recyclable (thermoplastic)
Industrially compostable
Recycling Code
7 (Other)
7
Carbon Footprint
Moderate to High
~1.6 kg CO₂e / kg
Bio-based Content
—
100 %