Comparison

POM Copolymer vs PETG

A side-by-side comparison of Polyoxymethylene Copolymer and Polyethylene Terephthalate Glycol.

Property

POM Copolymer

PETG

Physical

Density

1.40-1.41 g/cm³

1.27 g/cm³

Water Absorption (24h)

0.2-0.4 %

0.13 %

Transparency

Opaque

Transparent

Shrinkage

1.2-2.8 %

0.2 – 0.5 %

Mechanical

Young's Modulus

2.5-3.5 GPa

2.1 GPa

Tensile Strength

55-75 MPa

50 MPa

Elongation at Break

20-50 %

120 %

Impact Strength (Izod)

70-90 kJ/m

100 J/m

Flexural Strength

—

70 MPa

Thermal

Glass Transition Temperature

-50 to -10 °C

80 °C

Melting Point

155-165 °C

—

Continuous Service Temperature

80-100 °C

65 °C

Heat Deflection Temperature

90-120 °C (1.8 MPa)

70 °C

CTE

—

68 × 10⁻⁶ /K

Electrical

Dielectric Constant

3.7-4.1

3.3

Volume Resistivity

10^12-10^14 Ohm-cm

10¹⁴ Ω·cm

Dielectric Strength

15-25 kV/mm

—

Chemical resistance

Acids

Good

Bases

Good

Fair

Solvents

Excellent

—

UV Resistance

Fair (requires stabilization)

Fair

Alcohols

—

Good

Oils

—

Good

Sustainability

Recyclability

Recyclable

Recycling Code

7 (Other)

Carbon Footprint

Moderate

~2.7 kg CO₂e / kg

Bio-based Content

—

0 %