Comparison
rABS Injection Molding vs PLA
A side-by-side comparison of Recycled Acrylonitrile Butadiene Styrene and Polylactic Acid.
Physical
Density
1.04-1.08 g/cm³
1.24 g/cm³
Water Absorption (24h)
0.2-0.5 %
0.5 %
Transparency
Opaque
Semi-transparent
Shrinkage
0.5-0.8 %
0.3 – 0.5 %
Mechanical
Young's Modulus
1.8-2.5 GPa
3.5 GPa
Tensile Strength
35-50 MPa
50 – 65 MPa
Elongation at Break
5-20 %
6 %
Impact Strength (Izod)
20-50 J/m
16 J/m
Flexural Strength
—
80 MPa
Thermal
Glass Transition Temperature
100-110 °C
60 °C
Melting Point
N/A (amorphous)
150 – 160 °C
Continuous Service Temperature
70-85 °C
45 °C
Heat Deflection Temperature
80-95 °C (0.45 MPa)
55 °C
Electrical
Dielectric Constant
2.7-3.0
3.0
Volume Resistivity
10^15-10^17 Ohm·cm
10¹⁴ Ω·cm
Dielectric Strength
15-25 kV/mm
—
Chemical resistance
Acids
Fair resistance
Fair
Bases
Fair resistance
Poor
Solvents
Good resistance to weak acids and bases, poor to strong solvents
—
UV Resistance
Poor (requires additives)
Poor
Alcohols
—
Fair
Hydrolysis
—
Poor
Sustainability
Recyclability
Recyclable (check local facilities)
Industrially compostable
Recycling Code
7 (Other)
7
Carbon Footprint
Lower than virgin ABS
~1.6 kg CO₂e / kg
Bio-based Content
—
100 %