Comparison
rEVA Flexible Clear vs Polycarbonate
A side-by-side comparison of Recycled Ethylene Vinyl Acetate Flexible Clear and Polycarbonate.
Physical
Density
0.920-0.950 g/cm³
1.20 g/cm³
Water Absorption (24h)
0.1-0.3 %
0.15 %
Transparency
Good
Transparent (88% light transmission)
Shrinkage
2.0-5.0 %
0.5 – 0.8 %
Mechanical
Young's Modulus
0.05-0.20 GPa
2.3 – 2.4 GPa
Tensile Strength
5-15 MPa
60 – 70 MPa
Elongation at Break
300-800 %
100 – 150 %
Impact Strength (Izod)
N/A (flexible grade)
600 – 900 J/m
Flexural Strength
—
90 – 100 MPa
Hardness (Rockwell M)
—
70
Thermal
Glass Transition Temperature
-50 to -80 °C (depends on VA content)
147 °C
Melting Point
45-70 °C (depends on VA content)
—
Continuous Service Temperature
30-50 °C
115 – 130 °C
Heat Deflection Temperature
N/A
130 – 140 °C
Thermal Conductivity
—
0.20 W/m·K
CTE
—
65 – 70 × 10⁻⁶ /K
Electrical
Dielectric Constant
2.8-3.5
2.9 – 3.0
Volume Resistivity
>10^14 Ohm·cm
10¹⁶ Ω·cm
Dielectric Strength
10-20 kV/mm
15 kV/mm
Chemical resistance
Acids
Good resistance
—
Bases
Good resistance
Poor
Solvents
Poor resistance to organic solvents
—
UV Resistance
Poor (requires stabilization)
Poor (unless coated)
Acids (dilute)
—
Good
Alcohols
—
Fair
Oils
—
Good
Gasoline
—
Fair
Acetone
—
Poor (attacks)
Sustainability
Recyclability
Recyclable (check local facilities)
Recyclable
Recycling Code
4 (LDPE) or 7 (Other)
7
Carbon Footprint
Lower than virgin EVA
~5 kg CO₂e / kg
Bio-based Content
—
0 – 50 % (bio grades)