Comparison
rPS General Purpose vs PLA
A side-by-side comparison of Recycled General Purpose Polystyrene and Polylactic Acid.
Physical
Density
1.04-1.06 g/cm³
1.24 g/cm³
Water Absorption (24h)
0.03-0.05 %
0.5 %
Transparency
Good to Excellent
Semi-transparent
Shrinkage
0.5-0.8 %
0.3 – 0.5 %
Mechanical
Young's Modulus
2.8-3.5 GPa
3.5 GPa
Tensile Strength
40-55 MPa
50 – 65 MPa
Elongation at Break
1-4 %
6 %
Impact Strength (Izod)
10-20 J/m
16 J/m
Flexural Strength
—
80 MPa
Thermal
Glass Transition Temperature
90-100 °C
60 °C
Melting Point
N/A (amorphous)
150 – 160 °C
Continuous Service Temperature
60-70 °C
45 °C
Heat Deflection Temperature
80-90 °C (0.45 MPa)
55 °C
Electrical
Dielectric Constant
2.5-2.7
3.0
Volume Resistivity
10^16-10^18 Ohm·cm
10¹⁴ Ω·cm
Dielectric Strength
15-20 kV/mm
—
Chemical resistance
Acids
Good resistance
Fair
Bases
Good resistance
Poor
Solvents
Poor resistance to aromatic and chlorinated hydrocarbons
—
UV Resistance
Poor
Poor
Alcohols
—
Fair
Hydrolysis
—
Poor
Sustainability
Recyclability
Recyclable (check local facilities)
Industrially compostable
Recycling Code
6 (PS)
7
Carbon Footprint
Lower than virgin PS
~1.6 kg CO₂e / kg
Bio-based Content
—
100 %