Comparison
Regenerated Cellulose Coated vs PLA
A side-by-side comparison of Regenerated Cellulose, Coated Grade FF and Polylactic Acid.
Physical
Density
1.45 g/cm³ (base film)
1.24 g/cm³
Water Absorption (24h)
Reduced by coating
0.5 %
Transparency
Exceptional
Semi-transparent
Shrinkage
4.0-8.0 %
0.3 – 0.5 %
Mechanical
Young's Modulus
10 GPa (base film)
3.5 GPa
Tensile Strength
100 MPa (base film)
50 – 65 MPa
Elongation at Break
2.0 % (base film)
6 %
Impact Strength (Izod)
0.05 J/cm (base film)
16 J/m
Flexural Strength
—
80 MPa
Thermal
Glass Transition Temperature
100-150 °C (base film)
60 °C
Melting Point
None (decomposes)
150 – 160 °C
Continuous Service Temperature
60 °C
45 °C
Heat Deflection Temperature
60 °C
55 °C
Electrical
Dielectric Constant
6.0 (base film)
3.0
Volume Resistivity
10¹⁰ Ω·cm (base film)
10¹⁴ Ω·cm
Dielectric Strength
20 kV/mm (base film)
—
Chemical resistance
Acids
Good resistance
Fair
Bases
Good resistance
Poor
Solvents
Insoluble in common organic solvents, but sensitive to moisture
—
UV Resistance
Moderate
Poor
Alcohols
—
Fair
Hydrolysis
—
Poor
Sustainability
Recyclability
Biodegradable (compost)
Industrially compostable
Recycling Code
7 (Other)
7
Carbon Footprint
Moderate
~1.6 kg CO₂e / kg
Bio-based Content
—
100 %