Automotive Sealing Grade Thermoplastic Vulcanizate (TPV) vs PETG
A side-by-side comparison of Thermoplastic Vulcanizate (TPV) - Automotive Sealing Grade and Polyethylene Terephthalate Glycol.
Physical
Density
0.90 - 0.95 g/cm³
1.27 g/cm³
Water Absorption (24h)
0.2 %
0.13 %
Transparency
Opaque
Transparent
Shrinkage
1.5 - 2.2 %
0.2 – 0.5 %
Mechanical
Young's Modulus
0.02 - 0.04 GPa
2.1 GPa
Tensile Strength
12 - 20 MPa
50 MPa
Elongation at Break
350 - 500 %
120 %
Impact Strength (Izod)
Good
100 J/m
Flexural Strength
—
70 MPa
Thermal
Glass Transition Temperature
-45 to -30 °C
80 °C
Melting Point
N/A
—
Continuous Service Temperature
-50 to 135 °C
65 °C
Heat Deflection Temperature
60 - 80 °C
70 °C
CTE
—
68 × 10⁻⁶ /K
Electrical
Dielectric Constant
2.9 - 3.4
3.3
Volume Resistivity
10^13 - 10^15 Ohm-cm
10¹⁴ Ω·cm
Dielectric Strength
22 - 28 kV/mm
—
Chemical resistance
Acids
Good
Good
Bases
Good
Fair
Solvents
Resists automotive fluids, water, mild acids/bases; swells in many hydrocarbon solvents
—
UV Resistance
Excellent
Fair
Alcohols
—
Good
Oils
—
Good
Sustainability
Recyclability
Recyclable (thermoplastic processing)
Recyclable
Recycling Code
7 (Other)
1
Carbon Footprint
Moderate
~2.7 kg CO₂e / kg
Bio-based Content
—
0 %