Asahi Kasei · POM (Delrin)
Tenac 3010
Acetal (POM) Homopolymer
Commercial, Active, Africa & Middle East, Asia Pacific, Europe, North America, Creep Resistant, Fatigue Resistant, Good Dimensional Stability, Good Toughness, High Impact Resistance, High Stiffness, High Strength, High Viscosity, Homopolymer
Manufacturer
Asahi Kasei
Base polymer
POM (Delrin)
Status
active
Technical properties
| Density/Specific Gravity | 1.42 g/cm3 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16kg) | 2.8 g/10 min |
| Molding Shrinkage-Flow | 1.8 to 2.2 % |
| Water Absorption (24hr, 23°C, 50%RH) | 0.20 % |
| Tensile Modulus | 3000 MPa |
| Tensile Stress Yield | 70.0 MPa |
| Tensile Elongation (Break) | 50 % |
| Flexural Modulus | 2800 MPa |
| Flexural Strength | 96.0 MPa |
| Taber Abrasion Resistance | 13.0 mg |
| Charpy Notched Impact Strength | 13 kJ/m2 |
| Notched Izod Impact | 120 J/m |
| Rockwell Hardness M-Scale | 94 |
| Rockwell Hardness R-Scale | 120 |
| Deflection Temperature Under Load (0.45MPa, Unannealed) | 172 °C |
| Deflection Temperature Under Load (1.8MPa, Unannealed) | 133 °C |
| CLTE-Flow | 1.0E-4 cm/cm/°C |
| Specific Heat | 1470 J/kg/°C |
| Thermal Conductivity | 0.23 W/m/K |
| Surface Resistivity | 1.0E+16 to 1.0E+17 ohms |
| Volume Resistivity (23°C) | 1.0E+15 to 1.0E+16 ohms·cm |
| Dielectric Strength | 18 kV/mm |
| Dielectric Constant (23°C, 1MHz) | 3.80 |
| Dissipation Factor (23°C, 1MHz) | 7.0E-3 |
| Arc Resistance | 250 sec |
| Flame Rating (1.5mm) | HB |
Indicative values. Always consult the manufacturer's official datasheet before specification.
Tenac 3010 equivalents
No verified equivalents indexed yet.
Typical applications
Automotive ApplicationsBearingsConveyor PartsEngineering PartsFastenersGears