Chi Mei · ABS
PA-757 ABS
Polylac
Polymer, Thermoplastic, ABS Polymer, Acrylonitrile Butadiene Styrene (ABS)
Manufacturer
Chi Mei
Base polymer
ABS
Status
active
Technical properties
| Density | 1.05 g/cc |
| Linear Mold Shrinkage | 0.0030-0.0070 cm/cm |
| Melt Flow (Load 5.00kg, Temperature 200℃) | 1.8 g/10 min |
| Melt Flow (Load 10.0kg, Temperature 220℃) | 22 g/10 min |
| Hardness, Rockwell R | 116 |
| Ball Indentation Hardness | 110 MPa |
| Tensile Strength at Break | 37.0 MPa |
| Tensile Strength, Yield | 54.0 MPa |
| Elongation at Break | 20% |
| Flexural Strength | 76.0 MPa |
| Flexural Modulus | 2.20 GPa |
| Izod Impact, Notched (Thickness 6.35mm) | 1.83 J/cm |
| Izod Impact, Notched (Thickness 3.17mm) | 2.05 J/cm |
| Izod Impact, Notched (ISO) | 14.0 kJ/m² |
| Izod Impact, Unnotched (ISO) | NB |
| Charpy Impact Unnotched | NB |
| Charpy Impact, Notched (Metric) | 1.50 J/cm² |
| Impact Flexural Test Notched | 11.0 KJ/m² |
| Impact Flexural Test Unnotched | NB |
| Deflection Temperature at 1.8MPa (264psi) (unannealed) | 88.0 ℃ |
| Deflection Temperature at 1.8MPa (264psi) (annealed) | 98.0 ℃ |
| Vicat Softening Point (Load 5.00kg, 50℃/hr) | 100 ℃ |
| Vicat Softening Point (Load 5.00kg, 120℃/hr) | 101 ℃ |
| Vicat Softening Point (Load 1.00kg, 50℃/hr) | 104 ℃ |
| Vicat Softening Point (Load 1.00kg, 120℃/hr) | 105 ℃ |
| Flammability, UL94 (Thickness 1.59mm) | HB |
Indicative values. Always consult the manufacturer's official datasheet before specification.
PA-757 ABS equivalents
No verified equivalents indexed yet.
Typical applications
Molded
Base polymer
ABS
See the full ABS technical sheet