EMS-Grivory · Grade
Grivory HT2V-3H
PA 6T/66
Grivory HT2V-3H is a 30 % glass fibre reinforced engineering thermoplastic material based on a semi-crystalline, partially aromatic copolyamde.
Manufacturer
EMS-Grivory
Status
active
Technical properties
| Tensile E-Modulus | 11000 MPa |
| Tensile strength at break | 175 MPa |
| Elongation at break | 2 % |
| Impact strength (Charpy, 23°C) | 45 kJ/m2 |
| Impact strength (Charpy, -30°C) | 40 kJ/m2 |
| Notched impact strength (Charpy, 23°C) | 9 kJ/m2 |
| Notched impact strength (Charpy, -30°C) | 98 kJ/m2 |
| Ball indentation hardness | 270 MPa |
| Melting point | 310 °C |
| Heat deflection temperature HDT/A (1.80 MPa) | 280 °C |
| Heat deflection temperature HDT/C (8.00 MPa) | 200 °C |
| Thermal expansion coefficient longitudinal (23-55°C) | 0.20 10^-4/K |
| Thermal expansion coefficient transverse (23-55°C) | 0.70 10^-4/K |
| Maximum usage temperature (long term) | 140 °C |
| Maximum usage temperature (short term) | 240 °C |
| Dielectric strength | 38 kV/mm |
| Comparative tracking index | 600 |
| Specific volume resistivity | 10^10 Ohm * m |
| Specific surface resistivity | 10^12 Ohm |
| Density | 1.42 g/cm3 |
| Flammability (UL94, 0.8mm) | HB |
| Water absorption (23°C/sat.) | 5.0 % |
| Moisture absorption (23°C/50% r.h.) | 1.8 % |
| Linear mould shrinkage (longitudinal) | 0.15 % |
| Linear mould shrinkage (transverse) | 0.80 % |
Indicative values. Always consult the manufacturer's official datasheet before specification.