Envalior · Grade
Pocan® B3235
PBT-GF30
Manufacturer
Envalior
Trade family
Pocan®
Status
active
Technical properties
| Melt volume-flow rate, MVR | 17 cm³/10min |
| Temperature | 260 °C |
| Load | 2.16 kg |
| Molding shrinkage, parallel | 0.4 % |
| Molding shrinkage, normal | 1.1 % |
| Tensile modulus | 9800 MPa |
| Stress at break | 145 MPa |
| Strain at break | 2.9 % |
| Tensile creep modulus, 1h | 9800 MPa |
| Tensile creep modulus, 1000h | 8900 MPa |
| Charpy impact strength, +23°C | 65 kJ/m² |
| Charpy impact strength, -30°C | 60 kJ/m² |
| Charpy notched impact strength, +23°C | 10 kJ/m² |
| Charpy notched impact strength, -30°C | 9.5 kJ/m² |
| Puncture energy, +23°C | 2.3 J |
| Melting temperature, 10°C/min | 225 °C |
| Temperature of deflection under load, 1.80 MPa | 210 °C |
| Temperature of deflection under load, 0.45 MPa | 220 °C |
| Coefficient of linear thermal expansion, parallel | 30 E-6/K |
| Coefficient of linear thermal expansion, normal | 110 E-6/K |
| Burning behavior at 1.5 mm nominal thickness | HB class |
| Thickness tested | 1.5 mm |
| Burning behavior at thickness h | HB class |
| Burning rate, FMVSS, thickness 1 mm | 46.2 mm/min |
| Oxygen index | 20 % |
| Relative permittivity, 100Hz | 4 |
| Relative permittivity, 1MHz | 3.8 |
| Dissipation factor, 100Hz | 30 E-4 |
| Dissipation factor, 1MHz | 180 E-4 |
| Volume resistivity | >1E13 Ohm*m |
| Surface resistivity | >1E15 Ohm |
| Electric strength | 30 kV/mm |
| Comparative tracking index | 400 |
| Water absorption | 0.4 % |
| Humidity absorption | 0.1 % |
| Density | 1530 kg/m³ |
| Injection molding, melt temperature | 260 °C |
| Injection molding, mold temperature | 80 °C |
Indicative values. Always consult the manufacturer's official datasheet before specification.