INEOS Styrolution · Grade
General Purpose, Unreinforced
SAN
Manufacturer
INEOS Styrolution
Trade family
Luran® 368R GP
Status
active
Technical properties
| Density | 1.06 g/cm3 |
| Tensile Strength, Ultimate | 75.0 MPa |
| Tensile Elongation at Break | 3.5 % |
| Tensile Modulus | 3.5 GPa |
| Flexural Modulus | 3.5 GPa |
| Flexural Yield Strength | 120 MPa |
| Notched Izod Impact | 20 J/m |
| Hardness, Rockwell M | 85 |
| Hardness, Rockwell R | 109 |
| Deflection Temperature at 0.45 MPa (6.6 psi) | 100 °C |
| Deflection Temperature at 1.8 MPa (264 psi) | 95.0 °C |
| Vicat Softening Point | 106 °C |
| Melting Point | 110 °C |
| CTE, linear, parallel to flow | 7.00E-05 cm/cm/°C |
| Specific Heat Capacity | 1.30 J/g-°C |
| Thermal Conductivity | 0.190 W/m-K |
| Dielectric Constant | 2.8 |
| Dielectric Strength | 20.0 kV/mm |
| Dissipation Factor | 0.0007 |
| Surface Resistivity | 1.00E+13 ohm |
| Volume Resistivity | 1.00E+15 ohm-cm |
| Water Absorption, 24 hours | 0.25 % |
| Water Absorption, Equilibrium | 0.45 % |
| Light Transmittance | 90 % |
| Refractive Index | 1.57 |
| Melt Flow Rate (MFR) | 20.0 g/10 min |
Indicative values. Always consult the manufacturer's official datasheet before specification.
General Purpose, Unreinforced equivalents
No verified equivalents indexed yet.
Typical applications
AppliancesAutomotiveBattery CasesBrushesClosuresCosmeticsCupsDishesDisplaysElectricalHousewaresLensesMedicalPackagingStationeryTrays