INEOS Styrolution · ABS
Terluran GP-35
ABS
Terluran® GP-35 is a high-flow, general purpose injection molding grade with good ductility, intended for moldings with thin walls and/or adverse flow length to wall ratio.
Manufacturer
INEOS Styrolution
Base polymer
ABS
Status
active
Technical properties
| Melt volume-flow rate, MVR | 34 cm³/10min |
| MVR, Temperature | 220 °C |
| MVR, Load | 10 kg |
| Tensile Modulus | 2300 MPa |
| Yield stress | 44 MPa |
| Yield strain | 2.4 % |
| Nominal strain at break | 12 % |
| Impact Strength (Charpy), +23℃ | 125 kJ/m² |
| Impact Strength (Charpy), -30℃ | 90 kJ/m² |
| Notched Impact Strength (Charpy), +23℃ | 19 kJ/m² |
| Notched Impact Strength (Charpy), -30℃ | 7 kJ/m² |
| Temp. of deflection under load (1.80MPa) | 92 °C |
| Temp. of deflection under load (0.45MPa) | 95 °C |
| Vicat softening temperature, 50°C/h 50N | 95 °C |
| Burning Behav. at 1.5mm Nom. Thickn. | HB class |
| Burning Behav. at 1.5mm Nom. Thickn., Thickness tested | 1.5 mm |
| Burning Behav. at 3.0mm Nom. Thickn. | HB class |
| Burning Behav. at 3.0mm Nom. Thickn., Thickness tested | 3.0 mm |
| Volume Resistivity | >1E13 Ohm*m |
| Surface Resistivity | 1E13 Ohm |
| Water Absorption | 0.95 % |
| Humidity absorption | 0.24 % |
| Density | 1040 kg/m³ |
| Density of melt | 934 kg/m³ |
| Thermal Conductivity of Melt | 0.18 W/(mK) |
| Spec. heat capacity of melt | 2300 J/(kgK) |
| Ejection temperature | 84 °C |
| Pre-drying, Temperature | 80 °C |
| Pre-drying, Time | 2 - 4 h |
| Melt temperature, range | 220 - 260 °C |
| Mold temperature, range | 30 - 80 °C |
Indicative values. Always consult the manufacturer's official datasheet before specification.
Terluran GP-35 equivalents
No verified equivalents indexed yet.
Typical applications
moldings with thin walls and/or adverse flow length to wall ratio