Kolon Industries · PA66
KOPA® KN333G33
PA66-GF33
Heat stabilized or stable to heat
Manufacturer
Kolon Industries
Base polymer
PA66
Status
active
Technical properties
| Mold Shrinkage, MD | 0.005 mm/mm |
| Tensile Strength | 196 MPa |
| Flexural modulus, 23°C | 8800 MPa |
| Charpy notched impact strength, +23°C | 12 kJ/m² |
| Flexural Modulus | 9316 MPa |
| Flexural Strength | 284 MPa |
| Rockwell Hardness | R 121 |
| Izod Impact notched, 1/8 in | 108 J/m |
| Melting temperature, 10°C/min | 255 °C |
| Temp. of deflection under load, 1.80 MPa | 240 °C |
| UL 94 Flame rating | HB |
| Thickness tested | 0.8 mm |
| Coefficient of Thermal Expansion, MD | 20 E-6/K |
| DTUL @ 66 psi | 250 °C |
| DTUL @ 264 psi | 247 °C |
| Melting Temperature | 255 °C |
| Dielectric Strength, Short Time | 21 kV/mm |
| Dielectric Constant, 1 MHz | 3.6 |
| Arc Resistance | 135 s |
| Density | 1390 kg/m³ |
| Pre-drying - Temperature | 80 - 100 °C |
| Pre-drying - Time | 4 - 5 h |
| Processing humidity | ≤0.05 % |
| Mold temperature | 60 - 80 °C |
| Zone 1 | 260 °C |
| Zone 2 | 280 °C |
| Zone 3 | 280 °C |
| Nozzle temperature | 285 °C |
Indicative values. Always consult the manufacturer's official datasheet before specification.
KOPA® KN333G33 equivalents
No verified equivalents indexed yet.
Typical applications
Automotive
Base polymer
PA66
See the full PA66 technical sheet
Manufacturer
Kolon Industries
Browse all indexed grades