Lanxess · PA66
Durethan B30S
PA6
PA 6, non-reinforced, injection molding
Manufacturer
Lanxess
Base polymer
PA66
Status
active
Technical properties
| Material Status | Commercial: Active |
| Availability | Latin America |
| Forms | Pellets |
| Processing Method | Injection Molding |
| Specific Gravity | 1.14 g/cm³ |
| Apparent Density | 0.70 g/cm³ |
| Molding Shrinkage, Across Flow (260℃, 3.00mm) | 1.2 % |
| Molding Shrinkage, Across Flow (120℃, 2 hr, 3.00mm) | 0.40 % |
| Molding Shrinkage, Flow (260℃, 3.00mm) | 1.0 % |
| Molding Shrinkage, Flow (120℃, 2 hr, 3.00mm) | 0.32 % |
| Water Absorption, Saturation (23℃) | 10 % |
| Water Absorption, Equilibrium (23℃, 50% RH) | 3.0 % |
| Tensile Modulus (23℃) | 3200 MPa |
| Tensile Modulus (-5℃) | 3200 MPa |
| Tensile Strength, Yield (23℃) | 80.0 MPa |
| Tensile Strength, Break (23℃) | 50.0 MPa |
| Tensile Elongation, Yield (23℃) | 4.0 % |
| Tensile Elongation, Break (23℃) | 35 % |
| Nominal Tensile Strain at Break (23℃) | 20 % |
| Flexural Modulus (23℃) | 2900 MPa |
| Flexural Strength (5.0% Strain, 23℃) | 115 MPa |
| Flexural Strength (3.5% Strain) | 95.0 MPa |
| Flexural Strength (23℃) | 110 MPa |
| Flexural Strain at Flexural Strength (23℃) | 6.0 % |
| Film Puncture Energy | 12.0 J |
| Film Puncture Force | 5140 N |
| Charpy Notched Impact Strength (-30℃) | <10 kJ/m² |
| Charpy Notched Impact Strength (23℃) | <10 kJ/m² |
| Charpy Unnotched Impact Strength (-30℃) | No Break |
| Charpy Unnotched Impact Strength (23℃) | No Break |
| Notched Izod Impact (23℃, 3.18mm) | 59 J/m |
| Notched Izod Impact (23℃) | <10 kJ/m² |
| Unnotched Izod Impact Strength (-30℃) | No Break |
| Unnotched Izod Impact Strength (23℃) | No Break |
| Ball Indentation Hardness | 140 MPa |
| Deflection Temperature Under Load (0.45MPa, Unannealed, 3.99mm) | 180 ℃ |
| Deflection Temperature Under Load (0.45MPa, Unannealed) | 160 ℃ |
| Deflection Temperature Under Load (1.8MPa, Unannealed, 3.99mm) | 60.0 ℃ |
| Deflection Temperature Under Load (1.8MPa, Unannealed) | 55.0 ℃ |
| Deflection Temperature Under Load (8.0MPa, Unannealed) | 45.0 ℃ |
| Vicat Softening Temperature | 200 ℃ |
| Melting Temperature | 222 ℃ |
| CLTE, Flow (23 to 55℃) | 1.0E-4 cm/cm/°C |
| CLTE, Transverse (23 to 55℃) | 1.1E-4 cm/cm/°C |
| RTI Elec (1.50mm) | 105 ℃ |
| RTI Imp (1.50mm) | 65.0 ℃ |
| RTI Str (1.50mm) | 75.0 ℃ |
| Surface Resistivity | 1.0E+13 to 1.0E+14 ohm |
| Volume Resistivity (23℃) | 1.0E+15 ohm·cm |
| Electric Strength (23℃, 1.00mm) | 30 kV/mm |
| Electric Strength (23℃, 3.00mm) | 30 kV/mm |
| Dielectric Constant (23℃, 50Hz) | 3.80 |
| Dielectric Constant (23℃, 1MHz) | 3.50 |
| Dielectric Constant (23℃, 100Hz) | 4.00 |
| Dissipation Factor (23℃, 50Hz) | 0.050 |
| Dissipation Factor (23℃, 100Hz) | 0.017 |
| Dissipation Factor (23℃, 1MHz) | 0.020 |
| Comparative Tracking Index, Solution A | 600 V |
| Comparative Tracking Index, Solution B | 600 V |
| Flame Rating (1.50mm) | V-2 |
| Flame Rating (3.00mm) | V-2 |
| Glow Wire Flammability Index (2.00mm) | 750 ℃ |
| Oxygen Index | 26 % |
| Burning Behavior (>1.00mm) | passed |
| ISO Shortname | PA6,GR,14-030 |
| Drying Temperature-Dry Air Dryer | 80.0 ℃ |
| Drying Time-Dry Air Dryer | 2.0 to 6.0 hr |
| Processing(Melt) Temp | 260 to 280 ℃ |
| Mold Temperature | 80.0 to 100 ℃ |
| Residual Moisture Content | 0.030 to 0.12 % |
Indicative values. Always consult the manufacturer's official datasheet before specification.
Durethan B30S equivalents
No verified equivalents indexed yet.
Typical applications
injection molding
Base polymer
PA66
See the full PA66 technical sheet
Manufacturer
Lanxess
Browse all indexed grades