LG Chem · ABS
LUPOS GP2200
Styrenics Compound
Manufacturer
LG Chem
Base polymer
ABS
Status
active
Technical properties
| Molding Type | Injection Molding |
| Detailed Composition | ABS+GF20% Compound |
| Description | General Purpose |
| Specific Gravity | 1.19 |
| Shrinkage, Flow | 0.3~0.5 % |
| Shrinkage, Cross-flow | 0.2~0.4 % |
| Melt Flow Rate | 2.2 g/10min |
| Water Absorption | 0.20 % |
| Tensile Strength @Break | 87 MPa |
| Tensile Elongation @Break | 2 % |
| Tensile Modulus | 6170 MPa |
| Flexural Strength | 111 MPa |
| Flexural Modulus | 5250 MPa |
| IZOD Impact Strength, Notched, 4.0mm, 23℃ | 7.2 kJ/m² |
| IZOD Impact Strength, Notched, 4.0mm, -30℃ | 7.2 kJ/m² |
| IZOD Impact Strength, Notched, 4.0mm, -40℃ | 6.2 kJ/m² |
| Charpy Impact Strength, Notched, 4.0mm, 23℃ | 8.0 kJ/m² |
| Charpy Impact Strength, Notched, 4.0mm, -30℃ | 6.8 kJ/m² |
| Charpy Impact Strength, Notched, 4.0mm, -40℃ | 6.5 kJ/m² |
| Rockwell Hardness | 115 R-Scale |
| Heat Deflection Temperature, 0.45MPa | 99 ℃ |
| Heat Deflection Temperature, 1.8MPa | 96 ℃ |
| Vicat Softening Temperature | 102 ℃ |
| Coefficient of Linear Thermal Expansion, Flow | 34 10⁻⁶m/m·℃ |
| Coefficient of Linear Thermal Expansion, Cross-flow | 89 10⁻⁶m/m·℃ |
| Flammability | 1.5mm, HB |
| Relative Temperature Index (Electrical, Min. Thickness) | 1.50 mm |
| Relative Temperature Index (Electrical, Temp) | 60 ℃ |
| Relative Temperature Index (Electrical, Max. Temp) | 60 ℃ |
| Relative Temperature Index (Electrical, Thickness) | 1.50 mm |
| Relative Temperature Index (Mechanical With Impact, Min. Thickness) | 1.50 mm |
| Relative Temperature Index (Mechanical With Impact, Temp) | 60 ℃ |
| Relative Temperature Index (Mechanical With Impact, Max. Temp) | 60 ℃ |
| Relative Temperature Index (Mechanical With Impact, Thickness) | 1.50 mm |
| Relative Temperature Index (Mechanical Without Impact, Min. Thickness) | 1.50 mm |
| Relative Temperature Index (Mechanical Without Impact, Temp) | 60 ℃ |
| Relative Temperature Index (Mechanical Without Impact, Max. Temp) | 60 ℃ |
| Relative Temperature Index (Mechanical Without Impact, Thickness) | 1.50 mm |
| Dielectric Constant | 3.2 |
| Dielectric Strength | 24 kV/mm |
Indicative values. Always consult the manufacturer's official datasheet before specification.
LUPOS GP2200 equivalents
No verified equivalents indexed yet.
Typical applications
AutoChassis & EngineDust CoverCap