SABIC · Polycarbonate
PC Lexan 9034-111
Polycarbonate, non-reinforced
Manufacturer
SABIC
Base polymer
Polycarbonate
Trade family
Lexan
Status
active
Technical properties
| Tensile Strength, Ultimate | 62.1 MPa |
| Tensile Strength, Yield | 65.5 MPa |
| Elongation at Break | > 100 % |
| Modulus of Elasticity | 2.34 GPa |
| Flexural Yield Strength | 93.1 MPa |
| Flexural Modulus | 2.34 GPa |
| Compressive Strength | 62.1 MPa |
| Shear Strength | 41.4 MPa |
| Hardness, Rockwell M | 70 |
| Hardness, Rockwell R | 120 |
| Izod Impact, Notched | 801 J/m |
| Izod Impact, Unnotched | No Break |
| Specific Gravity | 1.20 |
| Specific Volume | 0.833 cm^3/g |
| Water Absorption, 24 hrs | 0.15 % |
| Water Absorption, Equilibrium | 0.35 % |
| Water Absorption @ Sat. (23C) | 0.35 % |
| Linear Mold Shrinkage, Flow | 0.0050 - 0.0070 cm/cm |
| Melting Point | 288 - 316 °C |
| CTE, linear, x-dir | 69.3 µm/µm-°C |
| CTE, linear, y-dir | 69.3 µm/µm-°C |
| Thermal Conductivity | 0.190 W/m-K |
| Specific Heat Capacity | 1.20 J/g-°C |
| Thermal Diffusivity | 0.130 cm^2/s |
| Vicat Softening Point | 147 °C |
| HDT at 0.45 MPa (65 psi) | 138 °C |
| HDT at 1.82 MPa (264 psi) | 130 °C |
| Glass Transition Temp, Tg | 150 °C |
| Flammability, UL94 | HB |
| Refractive Index | 1.586 |
| Light Transmittance | 88 % |
| Haze | < 1 % |
| Dielectric Strength | 15.7 kV/mm |
| Dielectric Constant | 2.95 |
| Dissipation Factor | 0.0008 |
| Volume Resistivity | 1.00e+16 ohm-cm |
Indicative values. Always consult the manufacturer's official datasheet before specification.
PC Lexan 9034-111 equivalents
No verified equivalents indexed yet.
Typical applications
General Purpose
Base polymer
Polycarbonate
See the full PC technical sheet
Manufacturer
SABIC
Browse all indexed grades