Solvay · Grade
Amodel AS-1133 HS
polyphthalamide
Amodel AS-1133 HS is a 33% glass reinforced, heat stabilized polyphthalamide (PPA) resin that provides excellent structural integrity in molded parts.
Manufacturer
Solvay
Status
active
Technical properties
| Filler / Reinforcement | Glass Fiber, 33% Filler by Weight |
| Additive | Heat Stabilizer |
| Density | 1.44 g/cm³ |
| Water Absorption (24 hr) | 0.21 % |
| Tensile Modulus (Dry) | 13100 MPa |
| Tensile Modulus (Conditioned) | 13100 MPa |
| Tensile Stress at Yield (Dry) | 225 MPa |
| Tensile Stress at Break (Dry) | 221 MPa |
| Tensile Stress at Break (Conditioned) | 193 MPa |
| Tensile Elongation at Break (Dry) | 2.5 % |
| Tensile Elongation at Break (Conditioned) | 2.1 % |
| Flexural Modulus (Dry) | 10300 MPa |
| Flexural Modulus (Conditioned) | 10300 MPa |
| Flexural Stress (Load at Break) | 326 MPa |
| Flexural Stress at Yield (Dry) | 317 MPa |
| Flexural Stress at Yield (Conditioned) | 254 MPa |
| Compressive Strength (Dry) | 276 MPa |
| Compressive Strength (Conditioned) | 247 MPa |
| Shear Strength (Dry) | 101 MPa |
| Shear Strength (Conditioned) | 88.9 MPa |
| Poisson's Ratio | 0.41 |
| Charpy Notched Impact Strength (Dry) | 11 kJ/m² |
| Charpy Unnotched Impact Strength (Dry) | 82 kJ/m² |
| Notched Izod Impact (Dry) | 75 J/m |
| Unnotched Izod Impact (Dry) | 1000 J/m |
| Rockwell Hardness (R-Scale) (Dry) | 125 |
| Deflection Temperature Under Load (0.45 MPa, Annealed, 3.18mm) | 297 °C |
| Deflection Temperature Under Load (1.8 MPa, Annealed, 3.18mm) | 285 °C |
| Deflection Temperature Under Load (1.8 MPa, Annealed) | 277 °C |
| Melting Temperature | 310 °C |
| CLTE (Flow: 0 to 100°C) | 2.3E-5 cm/cm/°C |
| CLTE (Flow: 160 to 249°C) | 1.4E-5 cm/cm/°C |
| CLTE (Transverse: 0 to 100°C) | 5.9E-5 cm/cm/°C |
| CLTE (Transverse: 160 to 249°C) | 1.3E-4 cm/cm/°C |
| Volume Resistivity (Dry) | 1.0E+16 ohms-cm |
| Volume Resistivity (Conditioned) | 2.0E+15 ohms-cm |
| Dielectric Strength (3.18mm) (Dry) | 21 kV/mm |
| Dielectric Strength (3.18mm) (Conditioned) | 21 kV/mm |
| Dielectric Constant (60Hz) (Dry) | 4.40 |
| Dielectric Constant (60Hz) (Conditioned) | 4.70 |
| Dielectric Constant (1MHz) (Dry) | 4.20 |
| Dielectric Constant (1MHz) (Conditioned) | 4.30 |
| Dissipation Factor (60Hz) (Dry) | 5.0E-3 |
| Dissipation Factor (60Hz) (Conditioned) | 9.0E-3 |
| Dissipation Factor (1MHz) (Dry) | 0.017 |
| Dissipation Factor (1MHz) (Conditioned) | 0.022 |
| Arc Resistance | 140 sec |
| Comparative Tracking Index (CTI) | 550 V |
| Flame Rating (3.2 mm) | HB |
Indicative values. Always consult the manufacturer's official datasheet before specification.
Amodel AS-1133 HS equivalents
No verified equivalents indexed yet.