Ixef 1022
Polyarylamide
Ixef® 1022 is a 50% glass-fiber reinforced, general purpose polyarylamide compound that exhibits very high strength and rigidity.
Manufacturer
Solvay
Status
active
Technical properties
| Filler / Reinforcement | Glass Fiber, 50% Filler by Weight |
| Density | 1.64 g/cm3 |
| Molding Shrinkage | 0.10 to 0.30 % |
| Water Absorption (23℃, 24 hr) | 0.16 % |
| Moisture Absorption-Equil, 65%RH | 1.50 % |
| Tensile Modulus (Dry) | 20000 MPa |
| Tensile Modulus (Conditioned) | 20000 MPa |
| Tensile Stress at Break (Dry) | 280 MPa |
| Tensile Stress at Break (Conditioned) | 260 MPa |
| Tensile Strain at Break (Dry) | 1.9 % |
| Tensile Strain at Break (Conditioned) | 2.2 % |
| Flexural Modulus (Dry) | 19000 MPa |
| Flexural Strength (Dry) | 400 MPa |
| Notched Izod Impact (Dry) | 110 J/m |
| Unnotched Izod Impact (Dry) | 850 J/m |
| Heat Deflection Temperature (1.8MPa, Unannealed, Dry) | 230 ℃ |
| CLTE-Flow | 0.000015 cm/cm/℃ |
| Volume Resistivity (Dry) | 1.0E+13 ohm·cm |
| Electric Strength (Dry) | 31 kV/mm |
| Dielectric Constant (110 Hz, Dry) | 4.60 |
| Comparative Tracking Index (Dry) | 570 V |
| Dissipation Factor (Dry) | 0.017 |
| Flame Rating | HB |
| Oxygen Index (Dry) | 25 % |
| Drying Temperature | 120℃ |
| Drying Time | 0.50 to 1.5 hr |
| Rear Temperature | 250 to 260℃ |
| Front Temperature | 260 to 290℃ |
| Nozzle Temperature | 260 to 290℃ |
| Processing (Melt) Temp | 280℃ |
| Mold Temperature | 120 to 140℃ |
Indicative values. Always consult the manufacturer's official datasheet before specification.
Ixef 1022 equivalents