Solvay · Grade
Radel R-5100
PPSU
Radel R-5100 is an opaque, general purpose polyphenylsulfone (PPSU) for injection molding, offering exceptional hydrolytic stability and toughness superior to other high-temperature engineering resins.
Manufacturer
Solvay
Status
active
Technical properties
| Molding Shrinkage-Flow | 0.70% |
| Water Absorption(24 hr) | 0.37% |
| Tensile Modulus | 2340MPa |
| Tensile Strength Yield | 69.6MPa |
| Tensile Strength Break | 69.6MPa |
| Tensile Elongation Yield | 7.2% |
| Tensile Elongation Break | 60% |
| Flexural Modulus | 2410MPa |
| Flexural Strength(Yield) | 91.0MPa |
| Compressive Modulus | 1730MPa |
| Compressive Strength | 98.9MPa |
| Shear Strength | 62.7MPa |
| Poisson's Ratio | 0.42 |
| Notched Izod Impact | 690J/m |
| Tensile Impact Strength | 399kJ/m2 |
| Deflection Temperature Under Load (0.45MPa, Unannealed) | 214℃ |
| Deflection Temperature Under Load (1.8MPa, Unannealed) | 207℃ |
| Glass Transition Temperature | 220℃ |
| CLTE-Flow | 5.6E-5cm/cm/℃ |
| Thermal Conductivity | 0.35W/m/K |
| Volume Resistivity | 9.0E+15ohms·cm |
| Dielectric Strength | 14kV/mm |
| Dielectric Constant (60Hz) | 3.44 |
| Dielectric Constant (1kHz) | 3.40 |
| Flame Rating (0.750 mm, ALL colors) | V-0 |
| Oxygen Index | 38% |
| Refractive Index | 1.672 |
| Drying Temperature | 149℃ |
| Drying Time | 2.5 hr |
| Melt Temperature - Rear | 321℃ |
| Melt Temperature - Middle | 349℃ |
| Melt Temperature - Front | 349℃ |
| Processing (Melt) Temp | 343 to 388℃ |
| Mold Temperature | 138 to 163℃ |
| Back Pressure | 0.345 to 0.689MPa |
| Screw Compression Ratio | 2.2:1.0 |
Indicative values. Always consult the manufacturer's official datasheet before specification.
Radel R-5100 equivalents
No verified equivalents indexed yet.