Glass-Filled PA610 — Polyamide 610, Glass Fiber Reinforced
Glass-filled PA610 offers enhanced stiffness and mechanical strength, along with better dimensional stability due to its lower moisture absorption compared to standard polyamides. It's a good choice for applications requiring rigidity and resistance to moisture.
PA610-GFNylon 610
Manufacturers
2
Grades
2
Applications
4
Equivalents
2
Physical Properties
- Density
- 1.18-1.28 g/cm³
- Water Absorption (24h)
- 1.0-1.5 %
- Transparency
- Opaque
- Shrinkage
- 0.5-0.8 %
Mechanical Properties
- Young's Modulus
- 5.0-7.0 GPa
- Tensile Strength
- 80-100 MPa
- Elongation at Break
- 5-15 %
- Impact Strength (Izod)
- 20-30 kJ/m
Thermal Properties
- Glass Transition Temperature
- 50-60 °C
- Melting Point
- 210-220 °C
- Continuous Service Temperature
- 90-110 °C
- Heat Deflection Temperature
- 120-150 °C (1.8 MPa)
Electrical Properties
- Dielectric Constant
- 3.6-4.2
- Volume Resistivity
- 10^10-10^12 Ohm-cm
- Dielectric Strength
- 15-20 kV/mm
Chemical Resistance
- Acids
- Fair
- Bases
- Good
- Solvents
- Good
- UV Resistance
- Fair
Sustainability
- Recyclability
- Recyclable
- Recycling Code
- 7 (Other)
- Carbon Footprint
- Moderate
Manufacturing compatibility
Injection Molding
Applications
Electrical connectors
Gears
Housings
Industrial components
Available grades
PA610 GF30PA610 GF40