MJF PA12 Powder — Polyamide 12 Powder for Multi Jet Fusion
PA12 powder for HP Multi Jet Fusion (MJF) offers superior mechanical properties, excellent surface finish, and nearly isotropic strength due to the MJF process. It is ideal for producing high-quality, durable functional parts.
PA12Nylon 12 MJFPA12-MJF
Manufacturers
3
Grades
3
Applications
5
Equivalents
0
Physical Properties
- Density
- 1.01-1.02 g/cm³
- Water Absorption (24h)
- 0.2-0.5 %
- Transparency
- Opaque
- Shrinkage
- Moderate (0.6-1.2%)
Mechanical Properties
- Young's Modulus
- 1.6-2.1 GPa
- Tensile Strength
- 52-62 MPa
- Elongation at Break
- 22-35 %
- Impact Strength (Izod)
- 6-10 kJ/m²
Thermal Properties
- Glass Transition Temperature
- 45-55 °C
- Melting Point
- 175-185 °C
- Continuous Service Temperature
- 70-80 °C
- Heat Deflection Temperature
- 45-55 °C @ 0.45 MPa
Electrical Properties
- Dielectric Constant
- 3.5-4.0
- Volume Resistivity
- 10¹¹-10¹³ Ω·cm
- Dielectric Strength
- 16-22 MV/m
Chemical Resistance
- Acids
- Good resistance
- Bases
- Good resistance
- Solvents
- Resistant to oils, greases, fuels. Attacked by strong acids.
- UV Resistance
- Moderate
Sustainability
- Recyclability
- Recyclable (up to 50% reusability in MJF)
- Recycling Code
- 7 (Other)
- Carbon Footprint
- High
Manufacturing compatibility
Multi Jet Fusion (MJF)
Applications
Functional Prototypes
End-Use Parts
Complex Geometries
Snap-fits
Automotive
Available grades
PA12PA12-GB (Glass Bead filled)PA12-PA11 (Co-polymer)