Comparison
PA610 Low Absorption vs PEEK
A side-by-side comparison of Polyamide 610 Low Absorption and Polyether Ether Ketone.
Physical
Density
1.06-1.08 g/cm³
1.32 g/cm³
Water Absorption (24h)
1.0-1.5 %
0.15 %
Transparency
Opaque
Opaque (amber)
Shrinkage
1.2-1.8 %
1.1 – 1.4 %
Mechanical
Young's Modulus
1.5-2.0 GPa
3.6 GPa
Tensile Strength
60-70 MPa
100 MPa
Elongation at Break
150-250 %
50 %
Impact Strength (Izod)
40-60 kJ/m
55 J/m
Flexural Strength
—
170 MPa
Thermal
Glass Transition Temperature
50-60 °C
143 °C
Melting Point
210-220 °C
343 °C
Continuous Service Temperature
90-110 °C
260 °C
Heat Deflection Temperature
60-80 °C (1.8 MPa)
160 °C
Electrical
Dielectric Constant
3.5-4.0
3.2
Volume Resistivity
10^11-10^13 Ohm-cm
10¹⁶ Ω·cm
Dielectric Strength
15-20 kV/mm
—
Chemical resistance
Acids
Fair
Excellent
Bases
Good
Excellent
Solvents
Good (oils, greases, solvents)
Excellent
UV Resistance
Fair
Fair
Hydrolysis (steam)
—
Excellent
Sustainability
Recyclability
Recyclable
Recyclable (specialty)
Recycling Code
7 (Other)
7
Carbon Footprint
Moderate
~30 kg CO₂e / kg