Engineering Thermoplastics
PA610 Low Absorption — Polyamide 610 Low Absorption
PA610 is a semi-aromatic polyamide offering lower moisture absorption and better dimensional stability compared to PA6 and PA66. It also provides good chemical resistance and wear properties.
PA610Nylon 610
Manufacturers
2
Grades
2
Applications
4
Equivalents
0
Physical Properties
- Density
- 1.06-1.08 g/cm³
- Water Absorption (24h)
- 1.0-1.5 %
- Transparency
- Opaque
- Shrinkage
- 1.2-1.8 %
Mechanical Properties
- Young's Modulus
- 1.5-2.0 GPa
- Tensile Strength
- 60-70 MPa
- Elongation at Break
- 150-250 %
- Impact Strength (Izod)
- 40-60 kJ/m
Thermal Properties
- Glass Transition Temperature
- 50-60 °C
- Melting Point
- 210-220 °C
- Continuous Service Temperature
- 90-110 °C
- Heat Deflection Temperature
- 60-80 °C (1.8 MPa)
Electrical Properties
- Dielectric Constant
- 3.5-4.0
- Volume Resistivity
- 10^11-10^13 Ohm-cm
- Dielectric Strength
- 15-20 kV/mm
Chemical Resistance
- Acids
- Fair
- Bases
- Good
- Solvents
- Good (oils, greases, solvents)
- UV Resistance
- Fair
Sustainability
- Recyclability
- Recyclable
- Recycling Code
- 7 (Other)
- Carbon Footprint
- Moderate
Manufacturing compatibility
Injection MoldingExtrusion
Applications
Bristles
Filaments
Electrical connectors
Gears
Available grades
PA610 Standard NaturalPA610 Glass Filled